The Potential of Light Brick from Plywood Industrial Waste as Sound-Absorbing Construction Material
Abstract
This research aims to examine the potential of light bricks made from plywood industry waste as a construction material with sound-dampening capabilities. Plywood sawdust waste was chosen as a mixing material due to its abundant availability and its lightweight and porous characteristics, which are expected to enhance the acoustic performance of the bricks. In this study, variations in the composition of plywood powder in bricks were made with the aim of evaluating its effect on physical, mechanical, and acoustic properties. The materials needed for this research are sand, cement, water, and plywood powder. The process of mixing and molding the bricks is done manually. Bricks are dried for 28 days to ensure the mechanical strength and stability of the bricks. Testing was conducted to evaluate physical properties through mass measurement and density testing, mechanical properties through compressive strength testing, and acoustic properties through sound absorption coefficient testing at various frequencies. The research results show that the addition of plywood powder significantly affects the reduction of brick density, making it lighter compared to conventional bricks. Based on the compressive strength test results, it is known that the addition of plywood powder has reduced the compressive strength value of the brick. However, bricks with an additional 10% and 20% volume of plywood powder still meet the minimum compressive strength requirements based on SNI 03-0349-1989. Meanwhile, the results of the sound absorption coefficient test indicate that the increase in the sound absorption coefficient is not significant, presumably due to the structural properties of the bricks that still require porosity optimization. In conclusion, lightt bricks with plywood powder filler have the potential to be environmentally friendly and lightweight construction materials, but they require improvement in optimizing sound absorption for more specific applications in buildings with acoustic insulation needs.
Keywords
Full Text:
PDFReferences
Af’idah, N. (2020). Biokomposit dari Limbah Organik. Jombang: LPPM Unhasy Tebuireng Jombang.
Af’idah, N., Manasikana, O.A., & Mayasari, A. (2020). The Effect of Additional Corn Husk Toward The Mechanical Properties of Light Brick. Jurnal Pena Sains, 7(2), 88-95.
Annisa, N. (2022). Inovasi Material Komposit Sebagai Peredam. Thesis. Hasanuddin University.
Butar, R.B. (2018). Pemanfaatan Sekam Padi Sebagai Bahan Agregat Tambahan Untuk Pembuatan Batako yang Kedap Suara. Thesis. Medan Area University.
Fatkhuurohman, M.A., Supriyadi. (2013). Tingkat Redam Bunyi Suatu Bahan (Triplek, Gypsum, dan Styrofoam). Jurnal Fisika, 3(2), 138-143.
Hadi, T. (2014). Analisa Mix Design Batako dengan Penambahan Limbah Kayu Pada Kuat Tekan standar. Teknis, 9(3).
Hami, W.G., Alfa, A., & Kinanda, R. (2021). Pengaruh Pencampuran Serat Kulit Pinang dan Serbuk Gergaji Terhadap Kuat Tekan Batako. Selodang Mayang: Jurnal Ilmiah Badan Perencanaan Pembangunan Daerah Kabupaten Indragiri Hilir, 7(2), 69-76.
Hartono. (2020). Kajian Pemakaian Bata Semen dengan Agregat Limbah Gergajian Kayu Sebagai Bahan Dinding Konstruksi Gedung. Wahana Teknik Sipil: Jurnal Pengembangan Teknik Sipil, 16(2).
Hasibuan, T., & Fauzi, A. (2021). "Potensi Limbah Kayu dalam Produksi Material Konstruksi Berkelanjutan." Jurnal Teknik Lingkungan dan Material, 14(2), 35-42.
Kurniawan, A., & Sari, P. (2020). "Pengelolaan Limbah Industri Kayu Lapis: Potensi dan Tantangan." Jurnal Pengelolaan Lingkungan, 15(2), 110-119.
Lindawati, L., Yusrizal, Y., & Fitriadi, N. (2019). Uji Mampu redam Bunyi Pada Material Batu Marmer Aceh Selatan. Jurnal Abulyatama, 534-541.
Masthura, Daulay, A.H., & Lubis, D.F., (2021). Uji Mekanik Batako dengan Penambahan Serbuk Gergaji kayu Jati (Tectona Grandist). Jurnal Sains dan Pendidikan Fisika, 17(2), 153-158.
Mintarsih, TH. (2006). Panduan Praktis Pengelolaan Lingkungan Industri Plywood. Jakarta: Asdep. Bidang Pengendalian Pencemaran Agro Industri.
Nugroho, M.W. & Susilowati. (2023). Pengujian Statistik Kualitas Batako Bersubsidi Bonggol Jagung. Buletin Profesi Insinyur, 6(1), 44-49.
Nurcahyo, W. (2021). "Analisis Karakteristik Batako Ringan dengan Bahan Pengisi Organik." Jurnal Teknologi Material Bangunan, 17(1), 45-52.
Pratama, A., Karo, P.K., Sembiring, S. (2014). Pembuatan dan Karakterisasi Batako Ringan dengan Campuran Sekam Padi sebagai Bahan Pengisi untuk Konstruksi Bangunan Redam Suara. Jurnal Teori dan Aplikasi Fisika, 2(1), 49.
Purba, R. E. S., Irwan, & Nurmaidah. (2017). Pemanfaatan Limbah Serbuk Gergaji Kayu Sebagai Substitusi Campuran Bata Ringan Kedap Suara. JCEBT, 1(2), 87-95.
Purba, R.E.S., & Lubis K. (2017). Pemanfaatan Limbah Serbuk Gergaji Kayu sebagai Substitusi Campuran Bata Ringan Kedap Suara. Portal Jurnal Teknik Sipil, 9(2).
Purwanto, D. (2009). Analisa Jenis Limbah Kayu Pada Industri Pengolahan Kayu di Kalimantan Selatan. Jurnal Riset Industri Hasil Hutan, 1(1), 14-20.
Puspitarini, Y., Musthafa, F., & Yulianto, A. (2014). Koefisien Serap Bunyi Ampas tebu sebagai Bahan Peredam Bunyi. Jurnal Fisika, 4(2), 96-100.
Rahman, M., & Ismail, Z. (2017). "Efek Penambahan Bahan Berpori pada Material Konstruksi dalam Peningkatan Insulasi Suara." Journal of Building Acoustics, 8(4), 345-352.
Risandi, A., & Elvaswer. (2017). Koefisien Absorpsi Bunyi dan Impedansi Akustik dari Panel Serat Kulit Jeruk dengan Menggunakan Metode Tabung. Jurnal Fisika Unand, 6(4), 331-335.
Royani, I. F., Basuki, A., & Sunarmasto. (2014). Kajian Kuat Tekan, Kuat Tarik, Kuat Lentur dan Redaman Bunyi Pada panel Dinding Beton Ringan dengan Agregat Limbah Plastik PET dan Limbah Serbuk Kayu. e-Jurnal Matriks Teknik Sipil, 641-648.
Setyawan, T., & Mulyadi, H. (2018). "Inovasi Material Konstruksi Berkelanjutan di Era Modern." Jurnal Teknologi Bangunan, 12(1), 25-30.
Setyoningrum, A., Anisah, & Saefudin, A. (2023). Literature Review Pemanfaatan Limbah Kayu gergaji Sebagai Pengganti Agregat Halus dalam Pembuatan Batako. Jurnal Deformasi, 8(2), 126-131.
Simanjuntak, V.H., (2011). Pembuatan dan Karakterisasi Batako Ringan dengan Memanfaatkan sabut Kelapa Sebagai Agregat untuk Bahan Kedap Suara. Magister Thesis. Sumatera Utara University.
Subari, D., Udiansyah, Yanuwijayadi, B., & Setiawan, B. (2012). Efektifitas Pengelolaan Limbah Cair Pada Industri Kayu Lapis di Kalimantan Selatan. Buana Sains, 12(1), 99-108.
Sujarwata & Sarwi. (2006). Pemanfaatan Limbah Serbuk Gergaji Sebagai Bahan Peredam Bunyi. Jurnal Pendidikan Fisika. 4(2), 115-119.
Sujatmiko, Heri. (2016). Penelitian Pemanfaatan Serbuk Bekas Penggergajian Kayu Sebagai Bahan Substitusi Pembuatan Bata Beron (Batako) Untuk Pemasangan Dinding. 17 Agustus 1945 Banyuwangi Universitiy.
Suryani, T., & Harahap, N. (2020). "Studi Komparatif Batako Ringan dan Konvensional sebagai Material Konstruksi Ramah Lingkungan." Journal of Sustainable Construction, 11(3), 112-118.
Syahrun, Ahzan, S., & Pangga, D. (2019). Uji Tekan Batako Ringan dari Limbah Pengolahan Emas dengan Variasi Komposisi Abu Sekam Pagi. Jurnal Penelitian dan Pengkajian Ilmu Pendidikan: e-Saintika, 2(2), 120-126.
Widiastuti, R., & Puspitasari, M. (2019). Pengaruh Material Limbah pada Batako Ringan untuk Peningkatan Efisiensi Energi. Jurnal Energi Bangunan, 16(2), 67-75.
Wulandari, E., & Prasetyo, A. (2019). Ekonomi Sirkular dalam Pemanfaatan Limbah Kayu pada Industri Konstruksi. Jurnal Material dan Konstruksi, 22(3), 78-85.
DOI: https://doi.org/10.33394/j-ps.v12i4.13016
Refbacks
- There are currently no refbacks.
Copyright (c) 2024 Noer Af'idah, Andri Wahyu Wijayadi, Elly Indahwati
This work is licensed under a Creative Commons Attribution 4.0 International License.
J-PS (Prisma Sains: Jurnal Pengkajian Ilmu dan Pembelajaran Matematika dan IPA IKIP Mataram) p-ISSN (print) 2338-4530, e-ISSN (online) 2540-7899 is licensed under a Creative Commons Attribution 4.0 International License.