Perbandingan Kualitas Kertas Komposit dari Ampas Tebu dan Kertas Koran Berdasarkan Konsentrasi NaOH yang Berbeda

Shinta Damayanti, Entin Daningsih, Andi Besse Tenriawaru

Abstract


Paper is needed in large quantities so the need for wood as a raw material for paper is getting higher. Composite paper uses non-wood raw materials can be an alternative to make paper. Bagasse can be used as a substitute for wood fiber and reduce waste in the environment to make composite paper. Likewise, newsprint can be used as a mixture of composite paper. This study aims to compare the quality of composite paper from bagasse and newsprint mixtures using different concentrations of NaOH. The method was an experimental completely randomized design (CRD) consisting three treatments of NaOH (4, 6, and 8%) and 10 replications. The parameters measured were paper thickness, grammage, mass density, and tensile resistance, and were using SPSS ANOVA and continued with LSD test. Paper thickness is affected by the amount of cellulose that was degraded as well as paper grammage, paper thickness and grammage have higher values at the lowest concentration of NaOH (4%). Meanwhile, the tensile strength showed long cellulose had not been degraded much and resulted in higher tensile strength. This also resulted in mass density showing the highest density at the highest concentration of NaOH (8%). In conclusion, concentration of 4% NaOH resulted in paper thickness, grammage, and higher tensile strength compared to 6% and 8% NaOH concentrations. However, the highest mass density was influenced by 8% NaOH concentration compared to 6% and 4% NaOH concentrations.

Keywords


Composite Paper, Bagasse, Newsprint, NaOH Concentration.

Full Text:

Full Paper

References


Apriani, E., dan Kurniasari, H.D. (2018). Pembuatan Kertas Daur Ulang dari Limbah Serat Kelapa Muda dan Kertas Bekas sebagai Alternatif Kertas Seni untuk Industri. In Prosiding Seminar Nasional Aplikasi Sains & Teknologi (SNAST) (pp. 309-316). Yogyakarta, Indonesia: Program Studi Teknik Mesin, Universitas Proklamasi.

Fenny, F.O., Farma W., dan Fitriyano, G. (2016). Pengaruh Rasio Berat Kulit Pisang dengan Kertas Koran dan Batang Jagung dengan Kertas Koran terhadap Indeks Tarik dan Indeks Sobek Kertas Recycle. In Seminar Nasional Sains (pp. 1-7). Jakarta, Indonesia: Jurusan Teknik Kimia, Universitas Muhammadiyah Jakarta.

Ikhsan, M. (2018). Pengembangan Material Kertas Menggunakan Serat Sekam Padi dengan Variasi Konsentrasi NaOH 10%, 15%, dan 20%. In Publikasi Ilmiah (pp. 1-11). Surakarta, Indonesia: Program Studi Teknik Mesin, Universitas Muhammadiyah Surakarta.

Kementerian Perindustrian Republik Indonesia. (2016). Retrieved August 18, 2021, From Kemenperin. Interactwebsite: https://www.Kemenperin.Go.Id/Artikel/16596/2017,-RI-Produsen-Kertas-Nomor-6-Terbesar-Dunia.

Masitah, N. (2014). Pembuatan Pulp dari Serabut Gambas Tua Kering dengan Proses Alkali dengan Alkohol. Jurnal Teknik Kimia, 9(1), 27-32.

Mulyadi, A.F., Wijana, S., dan Pratama, A.Y. (2014). Penggandaan Skala pada Pembuatan Pulp dari Pelepah Nipah (Nypa fruticans). In Proceeding Icoa-APTA Indonesian Track (pp. 1-7). Malang, Indonesia: Jurusan Teknologi Industri Pertanian, Universitas Brawijaya.

Prasetyo, R.A., dan Mahmudi, H. (2021). Analisa Pengaruh Kecepatan Produksi terhadap Gramatur Pembuatan Kertas. Jurnal Mesin Nusantara, 4(2), 108-113.

Prasetyo, Y. (2014). Pemanfaatan Serat Pisang Abaka (Musa textilis Nee) dan Kertas HVS sebagai Kertas Seni. Skripsi. Institut Pertanian Bogor.

Pratiwi, R.C. (2015). Pemanfaatan Limbah Bulu Ayam dan Kulit Jagung sebagai Bahan Pembuatan Kertas Seni dengan Penambahan NaOH dan Pewarna Alami. In Publikasi Ilmiah (pp. 1-12). Surakarta, Indonesia: Fakultas Keguruan dan Ilmu Pendidikan, Universitas Muhammadiyah Surakarta.

Rahmawati, A., Kurniahu, H., Sriwulan, dan Andriani, R. (2021). Komparasi Kandungan Timbal (Pb) Kertas Bekas Mengandung Tinta Pasca Aplikasi Cairan Rumen Sapi Berdasarkan Lama Inkubasi. Bioscientist: Jurnal Ilmiah Biologi, 9(2), 477-482.

Ramadhany, P., dan Handoko, T. (2021). Pengaruh Kandungan Selulosa dan Lignin pada Pulp Kulit Pisang Kepok dalam Pembuatan Kertas Seni. In Prosiding Seminar Nasional Riset dan Teknologi Terapan (Ritektra) (pp. 1-5). Bandung, Indonesia: Program Studi Teknik Kimia, Universitas Katolik Parahyangan.

Ristianingsih, Y., Angreani, N., dan Fitriani, A. (2018). Proses Pembuatan Kertas dari Kombinasi Limbah Ampas Tebu dan Sekam Padi dengan Proses Soda. Chempublish Journal, 2(2), 21-32.

Setiati, R., Wahyuningrum, D., Siregar, S., dan Marhaendrajana, T. (2016). Optimasi Pemisahan Lignin Ampas Tebu dengan Menggunakan Natrium Hidroksida. ETHOS: Jurnal Penelitian dan Pengabdian Masyarakat, 2(2), 257-264.

Sukaryono, I.D., dan Loupatty, V.D. (2018). Karakteristik Kertas Berbahan Kertas Bekas dan Limbah Rumput Laut Eucheuma cottonii. Majalah Biam, 14(2), 81-85.

Sundari, E.M., Apriani, W., dan Suhendra. (2020). Uji Kekuatan Tarik Kertas Daur Ulang Campuran Ampas Tebu, Serabut Kelapa, dan Kertas Bekas. Jurnal Ilmiah Teknik Mesin, 6(1), 28-33.

Widyawati, A. (2016). Kualitas Kertas Seni Berbahan Baku Pelepah Tanaman Salak dengan Perlakuan Konsentrasi NaOH dan Konsentrasi Lem PVAc. In Publikasi Ilmiah (pp. 1-8). Surakarta, Indonesia: Program Studi Pendidikan Biologi, Universitas Muhammadiyah Surakarta.

Wijatmoko, J. (2018). Pengembangan Material Kertas Daur Ulang dengan Sabut Kelapa terhadap Beberapa Pengujian dengan Variasi Konsentrasi NaOH 2%, 4%, 6%, dan 8%. In Publikasi Ilmiah (pp. 1-17). Surakarta, Indonesia: Program Studi Teknik Mesin, Universitas Muhammadiyah Surakarta.

Yosephine, A., Gala, V., Ayucitra, A., dan Retnoningtyas, E.S. (2012). Pemanfaatan Ampas Tebu dan Kulit Pisang dalam Pembuatan Kertas Serat Campuran. Jurnal Teknik Kimia Indonesia, 1(2), 94-100.




DOI: https://doi.org/10.33394/bioscientist.v10i2.5424

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.

Creative Commons License
Bioscientist : Jurnal Ilmiah Biologi is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License

Editorial Address: Pemuda Street No. 59A, Catur Building Floor I, Mataram City, West Nusa Tenggara Province, Indonesia